Generic PP, High Crystal
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eDHPNe_Generic-PP-High-Crystal.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, High Crystal This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| 23°C | 0.900 - 0.920 | g/cm³ | ISO 1183 |
| -- | 0.900 - 0.914 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 1.5 - 46 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 13 - 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 1.3 - 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 84 - 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1490 - 2210 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 24.1 - 42.5 | MPa | ASTM D638 |
| Yield, 23°C | 25.6 - 40.5 | MPa | ISO 527-2 |
| 23°C | 27.5 - 38.2 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.9 - 6.0 | % | ASTM D638 |
| Yield, 23°C | 4.5 - 6.1 | % | ISO 527-2 |
| Fracture, 23°C | 20 - 500 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1130 - 2380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 35 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 16 - 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 124 - 136 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 99.4 - 123 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 70.0 - 158 | °C | ISO 306 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 69 - 95 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 179 - 190 | °C | |
| Middle Temperature | 199 - 220 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Mold Temperature | 39.8 - 60.0 | °C | |
| Injection Pressure | 75.8 - 172 | MPa | |
| Holding Pressure | 61.3 - 152 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, High CrystalThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GBF 3020 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| SLOVAMID® 6 NG1 GF 20 HLS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Sylvin 6065-85-LTGL Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Sylvin 9812-95 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| ALTECH® ABS A 2020/100 GF20 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |