Chemlon® 100 L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eCq0vG_Chemlon-100-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 100 L is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 100 L are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 50 | % | |
| Flexural Modulus | 2790 | MPa | ASTM D790 |
| Flexural Strength | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 218 | °C | |
| 1.8 MPa, Unannealed | 87.8 | °C | |
| Melting Temperature | 257 | °C | DSC |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | UL 746 | ||
| 0.810 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Imp | UL 746 | ||
| 0.810 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 85.0 | °C | |
| RTI Str | UL 746 | ||
| 0.810 mm | 95.0 | °C | |
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 95.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | V-2 | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 254 | °C | |
| Middle Temperature | 257 to 274 | °C | |
| Front Temperature | 263 to 282 | °C | |
| Nozzle Temperature | 263 to 279 | °C | |
| Processing (Melt) Temp | 263 to 279 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 655A | Celanese Corporation | TPEE | Riteflex® |
| THERMOLAST® K TF8WKF (Series: DW) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Generic EnBA | Generic | EnBA | Generic |
| Sylvin 2912-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ WCD891B resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |