LNP™ STAT-KON™ DE0049P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eCOhAh_LNPSTATKONDE0049Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DE0049P is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. Also known as: LNP* STAT-KON* Compound DC-1004 EP FR Product reorder name: DE0049P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.56 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.14 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16500 | MPa | ASTM D638 |
| -- | 16000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 137 | MPa | ASTM D638 |
| Fracture | 132 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 0.90 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12400 | MPa | ASTM D790 |
| -- | 13200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 219 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 139 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 D36 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| SureSpec IP-350NA | Genesis Polymers | PP Impact Copolymer | SureSpec |
| Grilamid® LVX-65H SST black 9288 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| KumhoSunny PC/AES HEC0275 | Shanghai KumhoSunny Plastics Co., Ltd. | AES+PC | KumhoSunny PC/AES |
| LONGLITE® PBT 7330H-104F | CCP Group | ABS+PBT | LONGLITE® PBT |