Borealis PP BJ100HP
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eBtequ_Borealis-PP-BJ100HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BJ100HP is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process. The product is available in natural colour. BJ100HP is equipped with an additive package for optimum coupling between polymer matrix and glass fibres. The interaction leads to optimum stiffness and impact strength of the components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.904 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 90 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 25.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 1250 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 41 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 2.5 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A |
| -- | 72.0 | °C | ISO 306/B |
| Melt Energy | 105 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 3.00 - 6.00 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ EPDM666G33-BK09 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| Silopren® LSR 4060 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Witcom ABS 3L1 | Witcom Engineering Plastics B.V. | ABS | Witcom ABS |
| APEX® 90-A471RC-75NT | Teknor Apex Company | PVC, Flexible | APEX® |
| IZTAVIL P-250 GP | Mexichem Corporativo | PVC Homopolymer | IZTAVIL |