Ebalta GM 986-1 / Comp. A+B

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Ebalta Kunststoff GmbH
Trademark:	Ebalta
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eBt1hZ_Ebalta-GM-986-1-Comp-A-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
GM 986-1 Comp. B (Amine) can be subject to colour variations due to raw materials, but these colour variations have no influence on the quality and the properties of the product. This material is most suitable for high pressure moulding plants with high moulding pressure and temperature resistance. For application at 60°C Shore hardness D is between 60-62! The postcured material is not UV stable and darkens by and by. However according to our experience the change in colour does not affect its utilizability. As bonding agent on aluminium support we recommend our PU coupling paste KP 8. The material is also dimensionally stable at high temperatures. At a mould temperature of approx. 60°C a Shore hardness D of 62-64 will still be reached. Applications Foundry patterns Pattern plates fixtures Properties non-toxic according to regulations for hazardous material Shore D hardness approx. 70 dimensionally stable at high temperatures hard flexible well castable abrasion resistant

Message

GM 986-1 Comp. B (Amine) can be subject to colour variations due to raw materials, but these colour variations have no influence on the quality and the properties of the product.
This material is most suitable for high pressure moulding plants with high moulding pressure and temperature resistance. For application at 60°C Shore hardness D is between 60-62!
The postcured material is not UV stable and darkens by and by. However according to our experience the change in colour does not affect its utilizability.
As bonding agent on aluminium support we recommend our PU coupling paste KP 8.
The material is also dimensionally stable at high temperatures. At a mould temperature of approx. 60°C a Shore hardness D of 62-64 will still be reached.

Applications

Foundry patterns

Pattern plates

fixtures

Properties

non-toxic according to regulations for hazardous material

Shore D hardness approx. 70

dimensionally stable at high temperatures

hard flexible

well castable

abrasion resistant

General Information
Features	Good dimensional stability Good flexibility Good wear resistance Non-toxic
Appearance	Yellow
Processing Method	Casting

Hardness	Nominal Value		Test Method
Durometer Hardness (Shore D)	68 - 72		ISO 7619

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	30.0 - 40.0	MPa	ISO 527-2
Tensile Strain (Break)	130 - 170	%	ISO 527-2
Flexural Modulus	750 - 950	MPa	ISO 178
Flexural Stress	30.0 - 40.0	MPa	ISO 178
Flexural Strain at Flexural Strength	7.5 - 8.5	%	ISO 178

Thermoset	Nominal Value	Unit
Thermoset Components
Resin	Mixing ratio by weight: 100
Hardening method	Mixing ratio by weight: 26

Additional Information
Wear jet test : 35 W(V/t) [mm³/min] (internal tests)

Uncured Properties	Nominal Value	Unit
Density (20°C)	1.08 - 1.12	g/cm³
Viscosity (25°C)	5.3 - 6.3	Pa·s
Curing Time (20°C)	14 - 18	hr
Pot Life ¹(20°C)	16 - 20	min

Note Message
1 .	200 g

Resin Grade	Manufacturer	Category	Trademark
Royalite R6000	Spartech Plastics	PC	Royalite
Silopren® LSR 3696/25	Momentive Performance Materials Inc.	Silicone Rubber, LSR	Silopren®
Novalloy-A A5622	PlastxWorld Inc.	ABS+Nylon	Novalloy-A
Infino WP-1041	SAMSUNG SDI CO., LTD.	PC+ABS	Infino
LNP™ LUBRILOY™ Z20001 compound	SABIC Innovative Plastics	PPE+PS	LNP™ LUBRILOY™