Durethan® BC 550 Z DUSXBL 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eAERAw_Durethan-BC-550-Z-DUSXBL-900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.07 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 1.5 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.20 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 1.5 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | 430 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 50.0 | -- | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | -- | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 140 | 170 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 1800 | 470 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 55.0 | 14.0 | MPa | |
| 23°C 6 | 66.0 | 21.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | 9.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, BHR, 14-020 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.060 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | 25 | kJ/m² | |
| 23°C | 100 | 130 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 25 | 25 | kJ/m² | |
| 23°C | 85 | 110 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 67.0 | -- | J | |
| 23°C | 65.0 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 5700 | -- | N | |
| 23°C | 5000 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 53.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 219 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.4E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-11030-GF | Polylink Polymers (India) Ltd. | TPO | Polylink Polymer |
| Trilliant™ HC HC6620-0033 RS Natural | PolyOne Corporation | Nylon 66 | Trilliant™ HC |
| KOPA® KN135G33BLHS | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| IROGRAN® A 85 D 4968 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LNP™ STAT-KON™ AE003 compound | SABIC Innovative Plastics Europe | ABS | LNP™ STAT-KON™ |