ENGAGE™ 8402
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e9RBqV_ENGAGE-8402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8402 Polyolefin Elastomer is an ethylene-octene copolymer that offers excellent performance in durable, flexible injection molded industrial and consumer goods. ENGAGE 8402 provides high clarity in products requiring visual inspection and allows the use of hot runner molds to enhance production efficiency. In addition, its low density can help control resin and production costs, while reducing the weight of end products. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 2 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 88 | ||
| Shore D, 1 sec, Compression Molded | 34 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 6.70 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 11.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 910 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 72.6 | MPa | |
| 2% Secant : Compression Molded | 72.0 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 79.1 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -36.0 | °C | Internal Method |
| Vicat Softening Temperature | 72.2 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 96.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 80.4 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-315 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Celstran® PP-GF20-04 Black | Celanese Corporation | PP Homopolymer | Celstran® |
| Estane® CP80AS2 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| ImerPlast™ 20 | Imerys Minerals | Polyolefin, Unspecified | ImerPlast™ |
| Pearlbond™ ECO D900 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlbond™ ECO |