CERTENE™ EDF-230A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e8nk0Z_CERTENE-EDF-230A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EDF-230A is a certified prime grade 9% ETHYLENE VINYL ACETATE (EVA) copolymer often used in the production of specialty films needing excellent heat sealability and impact strength. EDF-230A applications include meat packaging and films requiring low temperature sealability. EDF-230A contains No slip and No antiblock. A melt temperature of 400°F or less is recommended to avoid polymer decomposition. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 31.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 27.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 330 | % | ASTM D882 |
| TD : Fracture, 38 µm | 650 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 250 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 120 | g | ASTM D1922 |
| TD : 38 µm | 100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525 |
| Melting Temperature | 99.0 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (38.0 µm) | 1.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.5 mils (38 µm) film; blow-up-ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 204 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 4204 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| DAI-EL™ G-101 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| KRATON® D1133 K | Kraton Polymers LLC | SBS | KRATON® |
| KumhoSunny ABS HFA700F | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LIM™ 6040 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | LIM™ |