InnoFR™ FX-8585
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoFR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e8ksgZ_InnoFR-FX-8585.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FX-8585 is a rigid polyurethane formulated for room temperature hand batch systems or vacuum assisted casting methods. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. FX-8585 passes UL 94-VO. It also meets the standards to pass FAR 25.853. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.23 | g/cm³ | |
| Hardener | 1.23 | g/cm³ | |
| Base Resin | 1.26 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 1.0 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1830 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 67 Mix Ratio by Weight: 56 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 90 to 210 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.45 | Pa·s | |
| 25°C 2 | 1.4 | Pa·s | |
| 25°C 3 | 3.8 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 5.5 to 8.5 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 90 | ASTM D2240 | |
| Tensile Strength | 39.3 | MPa | ASTM D638 |
| Tensile Elongation at Break | 6.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 180°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PP 502 | Shuman Plastics, Inc. | PP Copolymer | Shuman PP |
| VITAMIDE® BS10VN6551 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Titalon® 5300CF | Titan Plastics Compounds Co., Ltd. | PC | Titalon® |
| DURACON® SF-15LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Versaflex™ GP 2810-40N | PolyOne Corporation | TPE | Versaflex™ |