Estane® 2103-55D TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e8ansK_Estane-2103-55D-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
2103-55D is a thermoplastic polyurethane elastomer. Feature: Load bearing capacity |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (224°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.90 | % | ASTM D955 |
| Transverse flow | 0.60 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 96 | ASTM D2240 | |
| Shaw D | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (3.20 mm) | 172 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 g, H-22 Wheel) | 80.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% strain, 3.20mm | 13.4 | MPa | ASTM D412 |
| 100% strain, 3.20mm | 16.5 | MPa | ASTM D412 |
| 300% strain, 3.20mm | 31.7 | MPa | ASTM D412 |
| Tensile Strength (Break, 3.20 mm) | 44.1 | MPa | ASTM D412 |
| Tensile Elongation (Break, 3.20 mm) | 430 | % | ASTM D412 |
| Tensile Elongation at Break (3.20 mm) | 30 | % | ASTM D412 |
| Tear Strength 1(3.20 mm) | 158 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 25°C, 22 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 30 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 2 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 - 104 | °C | |
| Processing (Melt) Temp | 210 - 227 | °C | |
| Mold Temperature | 16.0 - 60.0 | °C |
| Injection instructions |
|---|
| Air Dew Point: <-40°C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA6 50 GF BLK | RTP Company | Nylon 6 | RTP |
| NORYL™ CRX1005 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Chemical Resources PA612153HS | Chemical Resources, Inc. | Nylon 612 | Chemical Resources |
| FERROCON® EPP99GA02BK | Ferro Corporation | PP Copolymer | FERROCON® |
| ADVANCENE™ bEE-4906-AAH | ETHYDCO | HDPE, HMW | ADVANCENE™ |