TPX®RT31XB is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in North America and is processed by film extrusion, fiber (spinning) extrusion or injection molding. TPX®The main features of RT31XB are:
TPX®The typical application areas of RT31XB are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 21 | g/10 min | ASTM D1238 |
| Spiral Flow 1 | 51.0 | cm | Internal method |
| Molding Shrinkage 2 | Internal method | ||
| Flow | 1.5 | % | Internal method |
| Transverse flow | 1.2 | % | Internal method |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 30.0 | MPa | ASTM D638 |
| Fracture, 23°C | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 12 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1600 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 174 | °C | ASTM D1525 |
| Melting Temperature | 233 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 65 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 94.0 | % | ASTM D1003 |
| Haze | 0.80 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 73°C, melt temperature: 310 to 320°C |
| 2 . | temperature range: 260 to 280°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProPell™ TPU 80A 0118J | Foster Corporation | Unspecified | ProPell™ |
| 4TECH® 9S33500 H | 4Plas | Polyphenylene, Unspecified | 4TECH® |
| INEOS PP 240-HP25 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| Karina GRAY PVC COMPOUND 750-18/328-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL® C 236 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |