EMERGE™ PC 6900 is a specially designed ignition-resistant polycarbonate alloy. It combines high flow, high heat and high strength together. It is especially suited for thin-wall applications and has excellent high gloss aesthetics. EMERGE PC 6900 has a UL94 V-0 rating at 1.0 mm. This material does not contain chlorine or bromine additives. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 70 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2650 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 1 |
| CLTE - Flow | 6.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 0.50 mm | V-2 | UL 94 | |
| 0.8 mm | V-1 | UL 94 | |
| 1.0 mm | V-0 | UL 94 | |
| 2.0 mm | 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 91 - 102 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 221 - 260 | °C | |
| Mold Temperature | 71 - 102 | °C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| 2 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2185 TFE 15 | RTP Company | PEI | RTP |
| TUFNYL® SFM 23 FRO GREY | SRF Ltd. | Nylon 6 | TUFNYL® |
| LNP™ LUBRICOMP™ KFL34XXC compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| HIPEX® HX8IDN (Series: HTR/OR) | KRAIBURG TPE | TPE | HIPEX® |
| LNP™ THERMOCOMP™ UF006S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |