POLYREX® PH-88S
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e6qIe1_POLYREX-PH-88S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYREX® PH-88S is a High Impact Polystyrene product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.6 | g/10 min | |
| 220°C/10.0 kg | 8.5 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 55 | % | ASTM D638 |
| Flexural Modulus 3(6.00 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength 4(6.00 mm) | 35.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.00 mm | 150 | J/m | |
| 23°C, 6.00 mm | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 80.0 | °C | |
| 1.8 MPa, Annealed | 94.0 | °C | |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 220 | °C | |
| Cylinder Zone 5 Temp. | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-S S1230 | PlastxWorld Inc. | PC+ABS | Novalloy-S |
| Geon™ Vinyl Wire & Cable WR3792CL | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| HIDEN® C100 | YUHWA Korea Petrochemical Ind. Co., Ltd. | CPE | HIDEN® |
| Hostacom EKG 286T Black | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Hytrel® 6356 | DuPont Performance Polymers | TPC-ET | Hytrel® |