NORYL GTX™ GTX951W resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e6ob7d_NORYLGTXGTX951Wresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A new high flow GTX designed for under-the-hood applications such as power distribution boxes, relay boxes and junction boxes. Developmental name EXNX0151. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/2.16 kg | 23 | g/10 min | ASTM D1238 |
| 280°C/5.0 kg | 64 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.4 - 1.7 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 - 1.5 | % | ASTM D955 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 2.0 | % | ISO 62 |
| 23°C, 24 hr 1 | 0.39 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2250 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 3 | 66.0 | MPa | ASTM D638 |
| Yield | 66.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 57.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 5 | 5.0 | % | ASTM D638 |
| Fracture 6 | 55 | % | ASTM D638 |
| Fracture | 51 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 100mm span 7 | 2550 | MPa | ASTM D790 |
| -- 8 | 2380 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 98.0 | MPa | ISO 178 |
| Fracture, 100mm span 9 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -20°C | 11 | kJ/m² | ISO 179/2C |
| 23°C | 21 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 210 | J/m | ASTM D256 |
| -30°C 10 | 8.1 | kJ/m² | ISO 180/4A |
| 23°C 11 | 14 | kJ/m² | ISO 180/4A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 32.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 196 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 12 | 181 | °C | ISO 75-2/Be |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 60 to 138°C | 1.7E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 60 to 138°C | 1.5E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.60 mm, in Oil) | 22 | kV/mm | ASTM D149 |
| Dissipation Factor (1 MHz) | 0.017 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 254 - 293 | °C | |
| Middle Temperature | 260 - 293 | °C | |
| Front Temperature | 266 - 293 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: .02 % |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 2.6 mm/min |
| 10 . | 63.5*12.7*3.2 |
| 11 . | 63.5*12.7*3.2 |
| 12 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SST 20 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| DJSilicone NE-Z270 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| GELAST GT807CA | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| EMOPLEN® CP GFR 20 FR V2 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| Halene P M365 | Haldia Petrochemicals Ltd. | PP Impact Copolymer | Halene P |