Generic PPS, Branched - Carbon Fiber
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e6G2K3_Generic-PPS-Branched---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS, Branched - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.39 - 1.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (23°C) | 0.15 - 0.25 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11100 - 28600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 119 - 210 | MPa | ASTM D638 |
| Fracture, 23°C | 113 - 204 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 0.74 - 2.0 | % | ASTM D638 |
| Fracture, 23°C | 0.56 - 0.81 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 18700 - 23500 | MPa | ASTM D790 |
| 23°C | 11000 - 30300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 46.0 - 312 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 - 64 | J/m | ASTM D256 |
| 23°C | 3.2 - 6.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 13 - 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 248 - 268 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-6 - 3.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.6E-6 - 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Rear Temperature | 309 - 310 | °C | |
| Middle Temperature | 326 - 327 | °C | |
| Front Temperature | 337 - 338 | °C | |
| Processing (Melt) Temp | 318 | °C | |
| Mold Temperature | 150 - 152 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS, Branched - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GFM 10/20 1 grey (4561) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Chiao Fu PA66/6 MB312GM33 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| FRIANYL® A3 GF25 V0P2 | Nilit Plastics | Nylon 66 | FRIANYL® |
| INEOS PP 100-GD02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| LNP™ VERTON™ MV008SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |