AT 193
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e68mPw_AT-193.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is suitable for use in Hot Melt Adhesive and coating applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.912 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 400 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 7.50 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 110 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 125 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 99.0 | °C | DSC |
| Additional Information |
|---|
| The value listed as Density-Specific Gravity, ASTM D1505, was also tested in accordance with ASTM D1928 ProcC Mod.Ring and Ball Softening Point: 109°C |
| Note Message | |
|---|---|
| 1 . | Type 4, 50mm/min |
| 2 . | Type 4, 50mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Capa™ 6200 | Perstorp Holding AB | PCL | Capa™ |
| Cheng Yu E500G10 | Cheng Yu Plastic Company Limited | PC+PET | Cheng Yu |
| DynaPath™ 3168 CF | Polymer Dynamix | PEI | DynaPath™ |
| Karina WHITE PVC COMPOUD -E 811-10/184-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ HF006EU compound | SABIC Innovative Plastics Europe | Nylon 11 | LNP™ THERMOCOMP™ |