Sumikon® PM-6930
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e5dQ37_SumikonPM6930.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-6930 (Type H Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good electronic property and heat resistance. This grade is official registered UL with V-0 (t=4.5). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.84 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.13 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.070 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 93.0 | MPa | JIS K6911 |
| Flexural Modulus | 14800 | MPa | JIS K6911 |
| Flexural Strength | 156 | MPa | JIS K6911 |
| Compressive Strength | 186 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.4 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 10 | kV/mm | JIS K6911 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 2.0E+13 | ohms | JIS K6911 |
| -- 3 | 8.0E+12 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.5 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 50A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Next Nylon 6 Prime Series NM30-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| HiFill® PA6/12 GF33 UV BK001 | Techmer Engineered Solutions | Nylon 612 | HiFill® |
| Lucent PC PC/PBT-0820 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| Daelim Po1y® XP6070 | DAELIM INDUSTRIAL CO., LTD. | mHDPE | Daelim Po1y® |