VENYL UFRHW308R - 7917
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e5Q70v_VENYL-UFRHW308R---7917.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UFRHW308R - 7917 is a halogen flame retardant compounds UL 94 V0 mineral filled reinforced polyamide 66 intended for injection moulding (specifically designed to fulfil norm such as: 2002/95/EC "ROHS"). APPLICATIONS VENYL UFRHW308R - 7917 has been developed especially for very demanding applications in electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL UFRHW308R - 7917 is available in natural (VENYL UFRHW308R) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.1 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 4700 | MPa | ISO 178 |
| Flexural Stress 1 | 132 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 37 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 255 to 275 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PP 80G4 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| CERTENE™ 740 | Muehlstein | ABS | CERTENE™ |
| EUROPLEX® Film HC 0F028 | Evonik Industries AG | PVDF+PMMA | EUROPLEX® Film |
| Hanwha Total PP CH72W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina CLEAR PVC COMPOUND 45/203-DA-ATB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |