Order Products : sales@su-jiao.com
Aegis® OXCE
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Honeywell |
| Trademark: | Aegis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3uts8_Aegis-OXCE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aegis® OXCE is an oxygen scavenging polyamide composition formulated specifically for use in high performance packaging applications where high gas barrier is required. This product is useful in injection and extrusion molding applications. Aegis® OXCE offers high oxygen barrier, even at high humidity, good carbon dioxide barrier, easy processing (particularly in the PET co-injection stretch blow molding process) excellent delamination resistance and clarity. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.75 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 260°C/2.16 kg | 13 | g/10 min | ISO 1133 |
| 280°C/2.16 kg | 23 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 90.2 | MPa | ISO 527-2 |
| Fracture | 53.7 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.4 | % | ISO 527-2 |
| Fracture | 130 | % | ISO 527-2 |
| Flexural Modulus | 2980 | MPa | ISO 178 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Transmission Rate 1(23°C, 80% RH) | 24.8 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen Transmission Rate (23°C, 80% RH, cast film) | < 0.047 | cm³/m²/24 hr | ASTM D3985 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.7 | °C | ASTM D648 |
| Glass Transition Temperature | 74.0 | °C | DSC |
| Melting Temperature (DSC) | 236 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 245 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 265 | °C | |
| Nozzle Temperature | 265 | °C |
| Injection instructions |
|---|
| Feed Zone: 35°CManifold: 265 to 280°C |
| Note Message | |
|---|---|
| 1 . | Oriented Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1935 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Mecoline IS RDX 5242 F | Melos GmbH | PVDF | Mecoline |
| Akulon® F160-Z | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Hifax TRC 790PHF 3004 BLK | LyondellBasell Industries | TPO (POE) | Hifax |
| Sylvin 8980-60 FU White 1306 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |