Generic TPC-ET
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3VHoV_Generic-TPC-ET.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPC-ET This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 1.07 - 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 2.0 - 31 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.50 - 34 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 3.91 - 32.4 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.58 - 2.0 | % | ASTM D955 |
| 23°C | 0.59 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.29 - 0.85 | % | ASTM D570 |
| 23°C, 24 hr | 0.28 - 0.70 | % | ISO 62 |
| Saturated, 23°C | 0.16 - 0.98 | % | ISO 62 |
| Equilibrium, 23°C | 0.29 - 0.51 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.41 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 27 - 81 | ASTM D2240 | |
| 23°C | 26 - 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 20.0 - 281 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 13.2 - 34.5 | MPa | ASTM D638 |
| Yield, 23°C | 14.6 - 36.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 0.300 - 55.1 | MPa | ASTM D638 |
| Fracture, 23°C | 9.66 - 53.8 | MPa | ISO 527-2 |
| 23°C | 1.30 - 31.0 | MPa | ASTM D638 |
| 23°C | 1.00 - 22.9 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 15 - 50 | % | ISO 527-2 |
| Fracture, 23°C | 4.0 - 810 | % | ASTM D638 |
| Fracture, 23°C | 250 - 750 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 50 - 900 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 28.0 - 1110 | MPa | ASTM D790 |
| 23°C | 17.0 - 209 | MPa | ISO 178 |
| Flexural Stress (23°C) | 1.00 - 4.63 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| 23°C | 29.4 - 251 | kN/m | ASTM D624 |
| 23°C | 40 - 190 | kN/m | ISO 34-1 |
| Bayshore Resilience | 40 - 65 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.4 - 120 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 8.5 - 81 | kJ/m² | ISO 180 |
| Tensile Impact Strength (23°C) | 179 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 46.0 - 140 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 44.7 - 116 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.7 - 55.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 39.9 - 46.4 | °C | ISO 75-2/A |
| Brittleness Temperature | -100 - -90.0 | °C | ISO 974 |
| Glass Transition Temperature | |||
| -- | -60.0 - 50.0 | °C | ISO 11357-2 |
| -- | 3.00 - 68.3 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 70.4 - 196 | °C | ASTM D1525 |
| -- | 86.2 - 211 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 185 - 219 | °C | |
| -- | 170 - 222 | °C | ISO 11357-3 |
| -- | 165 - 223 | °C | ASTM D3418 |
| -- | 173 - 220 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 1.0E-4 - 2.3E-4 | cm/cm/°C | ASTM E831 |
| Flow | 1.0E-4 - 2.6E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.4E-4 - 2.3E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 1.0E-4 - 2.3E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 50.0 - 90.0 | °C | UL 746 |
| RTI Imp | 50.0 - 85.0 | °C | UL 746 |
| RTI | 50.0 - 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+13 - 5.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+11 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 8.3E+10 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 26 | kV/mm | ASTM D149 |
| 23°C | 14 - 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 4.19 - 4.64 | ASTM D150 | |
| 23°C | 4.20 - 6.00 | IEC 60250 | |
| 23°C | 4.14 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 5.0E-3 - 0.041 | ASTM D150 | |
| 23°C | 7.0E-3 - 0.081 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | |||
| -- | 20 - 21 | % | ASTM D2863 |
| -- | 19 - 22 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 0.500 - 403 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 110 | °C | |
| Drying Time | 2.5 - 3.5 | hr | |
| Suggested Max Moisture | 0.010 - 0.082 | % | |
| Rear Temperature | 179 - 231 | °C | |
| Middle Temperature | 168 - 240 | °C | |
| Front Temperature | 196 - 245 | °C | |
| Nozzle Temperature | 210 - 247 | °C | |
| Processing (Melt) Temp | 180 - 246 | °C | |
| Mold Temperature | 22.5 - 50.0 | °C | |
| Back Pressure | 0.172 - 44.1 | MPa | |
| Screw Speed | 45 - 65 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPC-ETThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 110 | °C | |
| Drying Time | 2.5 - 3.5 | hr | |
| Suggested Max Moisture | 0.010 - 0.060 | % | |
| Cylinder Zone 1 Temp. | 190 - 230 | °C | |
| Cylinder Zone 2 Temp. | 199 - 235 | °C | |
| Cylinder Zone 3 Temp. | 190 - 240 | °C | |
| Cylinder Zone 4 Temp. | 210 - 240 | °C | |
| Adapter Temperature | 210 - 240 | °C | |
| Melt Temperature | 173 - 245 | °C | |
| Die Temperature | 199 - 240 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPC-ETThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP3004BUV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sumitomo Phenolic FM 4005X4648 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| GLS Nylon 66 LKG36 | GLS Polymers Pvt. Ltd. | Nylon 66 | GLS Nylon 66 |
| INNOPOL® PP CS 1-2110 AB | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Karina WHITE PVC COMPOUND 801-10/1-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |