Moplen EP310DC
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3SgH0_Moplen-EP310DC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP310DC is a low fluidity heterophasic copolymer designed for extrusion applications where smooth processability and high mechanical properties are of the utmost importance. Main applications are extrusion of film for heavy duty applications, adhesive tapes, lamination film and extrusion blow moulded containers for e.g. detergents. Moplen EP310DC is suitable for food contact. For regulatory information please refer to Moplen EP310DC Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | 420 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(60 µm) | 1200 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 60 µm | 27.0 | MPa | |
| Break, 60 µm | 49.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 60 µm | 7.0 | % | |
| Break, 60 µm | 830 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.2 | kJ/m² | |
| 0°C | 24 | kJ/m² | |
| 23°C | 79 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 72.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60.0 µm) | 12 | ASTM D2457 | |
| Haze (60.0 µm) | 60 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203D GB 20 TFE 15 | RTP Company | Nylon 612 | RTP |
| CYCOLAC™ DL100 resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |
| OP - PC - Filled 20GF | Oxford Polymers | PC | OP - PC - Filled |
| ESTOPLAST XU 6310GY01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| SQUARE® LIM6968-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |