Gravi-Tech™ GRV-TE1-090-W-NAT
| Category: | SIS , Styrene Isoprene Styrene Block Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Gravi-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3QkSG_Gravi-Tech-GRV-TE1-090-W-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Gravi-Tech™ polymer-metal composites offer a high-performance thermoplastic-based alternative to lead and traditional metals. Using a variety of metallic fillers, these compounds have densities similar to traditional metals, while offering design and processing flexibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 8.98 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 370 | % | ASTM D1708 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 1.57 | MPa | |
| 100% Strain | 1.54 | MPa | |
| 200% Strain | 1.41 | MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Processing (Melt) Temp | 163 to 204 | °C | |
| Mold Temperature | 15.6 to 37.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinblend® A783 | Shinkong Synthetic Fiber Corp. | PC+ABS | Shinblend® |
| Unichem 7002A-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Anjacom® R250-H/GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Grivory® GV-5H EF black 9915 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| MAJORIS G209 BLACK 8229 | AD majoris | PP, Unspecified | MAJORIS |