| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Youju New Materials Co., Ltd. |
| Trademark: | Paryls® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e33Evx_ParylsPPSUF1150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PARYLS® PPSU F1150 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PPSU F1150 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 10 - 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4, ISO 2577 | ||
| Transverse flow | 1.0 | % | ISO 294-4, ISO 2577 |
| Flow | 0.90 | % | ISO 294-4, ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2270 | MPa | ISO 527-2 |
| Tensile Stress | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.8 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 68 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 196 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 220 | °C | ISO 11357-2, DSC |
| CLTE - Flow (23°C) | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity 3 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength 4 | 44 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.5E-3 | IEC 60250 | |
| 1 MHz | 8.6E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 6.0 | hr | |
| Melt Temperature | 350 - 390 | °C | |
| Die Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 100V |
| 3 . | 100V |
| 4 . | K20/K20, (60*60*1 mm³) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® C3 GF 50 5 XTC natural (4946) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| LEXAN™ EM3110 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Loyblend® TY-1000 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+PBT | Loyblend® |
| Orevac® 18317 | Arkema | LLDPE | Orevac® |
| Sylvin 7833-75C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |