Maxxam™ FR PP FR 8-6 A NATURAL - ROHS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e2fN9M_Maxxam-FR-PP-FR-8-6-A-NATURAL---ROHS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 2.5 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 16.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength 4 | 27.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 210 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, All Colors | V-0 | ||
| 1.50 mm, All Colors | V-0 | ||
| 3.00 mm, All Colors | V-0 5VA | ||
| 2.20 mm, All Colors | 5VA |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 22CGF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| CALP HG2210B | Lion Idemitsu Composites Co., Ltd. | Nylon, Unspecified | CALP |
| Axiall PVC 16902 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LG PVC PB1120 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| LOTTMER HX-086AB | Lotte Chemical Corporation | TPE | LOTTMER |