Latamid 66 VH G/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e24tyr_Latamid-66-VH-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Thermally, glycol and hydrolisis stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.35 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9400 | MPa | |
| 60°C | 6200 | MPa | |
| 90°C | 4400 | MPa | |
| 120°C | 3500 | MPa | |
| 150°C | 2000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 145 | MPa | |
| Break, 60°C | 95.0 | MPa | |
| Break, 90°C | 75.0 | MPa | |
| Break, 120°C | 65.0 | MPa | |
| Break, 150°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.4 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 5.0 | % | |
| Break, 120°C | 5.0 | % | |
| Break, 150°C | 5.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1705 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Formolene® L62009X | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Hetron™ FR 650 INF-20 | Ashland Performance Materials | Polyester, TS | Hetron™ |
| INLUBE PA6SI2 | Infinity LTL Engineered Compounds | Nylon 6 | INLUBE |
| Plaskon PPF-165 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |