LNP™ LUBRICOMP™ UFL36S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e1vS7M_LNP-LUBRICOMP-UFL36S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound BGU Product reorder name: UFL36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.82 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.33 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12400 | MPa | ASTM D638 |
| -- | 9890 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 197 | MPa | ASTM D638 |
| Break | 196 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| -- | 11200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 281 | MPa | ASTM D790 |
| -- | 286 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.49 | ||
| Wear Factor - Washer | 6.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 255 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borlink™ LS4201S | Borealis AG | PE, Unspecified | Borlink™ |
| Ecomass® 2150TU96 | Ecomass Technologies | Nylon 66 | Ecomass® |
| Karina IVORY PVC COMPOUND -E 853-35/ 1-DY-IS(AS-80)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ QE002S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |
| TECACOMP® PA66 TC white 4040 | Ensinger GmbH | Nylon 66 | TECACOMP® |