Badamid® B70 SM-Z2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e0dYnl_Badamid-B70-SM-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6I Chemical modified standard injection moulding grade, very good toughness at low temperatures |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | 1150 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 70.0 | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 4.0 | 24 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 3(23°C) | 25 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 5 | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 222 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 70 | -- | °C | |
| some hours | 170 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 7 | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 8 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| -- | -- | 60 | kV/mm | |
| -- 9 | 100 | -- | kV/mm | |
| Relative Permittivity 10 | IEC 60250 | |||
| -- | 3.60 | -- | ||
| 1 MHz | -- | 6.90 | ||
| Dissipation Factor 11 | IEC 60250 | |||
| -- | -- | 0.30 | ||
| 1 MHz | 0.029 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 12 | HB | -- | ||
| 1.60 mm 13 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | 10 K/min, Compound for moulding |
| 7 . | 80x80x1 mm |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x0.8 mm |
| 13 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLEM® 66 GFR 15 IM | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| CERTENE™ LLHF-122XH | Muehlstein | LLDPE | CERTENE™ |
| Axiall PVC 8150 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 8354-62D Yellow 4193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® LSR6929-70AFC/BFC | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |