LNP™ KONDUIT™ PX13012 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e0Bhe6_LNP-KONDUIT-PX13012-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive, mineral filled PA6 compliant with ECO protocols, non-brominated, non chlorinated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow 1 | 0.70 | % | Internal Method |
| Flow : 24 hr | 0.55 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.65 | % | ASTM D955, ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 10400 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 68.0 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 1.2 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 11800 | MPa | ASTM D790 |
| -- 6 | 12000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 119 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 15 | J/m | ASTM D256 |
| 23°C 8 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D4812 |
| 23°C 9 | 9.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 203 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 203 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 160 | °C | ISO 75-2/Af |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ISO 22007-2 | ||
| -- 12 | 1.2 | W/m/K | |
| -- 13 | 5.5 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+14 | ohms | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 7.2 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 750 | °C | |
| 1.60 mm | 775 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| 12 . | through-plane, 60*60*3mm plaque |
| 13 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren TB500 | SINOPEC Shanghai Petrochemical Co. Ltd. | PP, Unspecified | Sanren |
| Yuyao PBT 3020G0 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| Akulon® Ultraflow K220-HGM44 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| MAJORIS FT200 | AD majoris | PP, Unspecified | MAJORIS |
| XYLEX™ X7200MR resin | SABIC Innovative Plastics Asia Pacific | PC+Polyester | XYLEX™ |