Clearflex® H&T FGH 196
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dzXMsG_Clearflex-H-T-FGH-196.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T FGH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. Films obtained from Clearflex H&T FGH 196 show excellent optical properties, a wide sealing window, both hot tack and heat seal, together with a low sealing initiation temperature (S.I.T.) and outstanding impact, puncture and Elmendorf tear resistance. Main Application Clearflex H&T FGH 196, for its overall characteristics, is the right choice for all applications, like silage stretch film, low thickness high clarity packaging film, requiring a superior mechanical strength. Moreover, the excellent sealability behaviour makes it ideal for lamination film production. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 170 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 8.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| MD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 500 | % | |
| TD : Break, 25 µm, Blown Film | 700 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 390 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 160.0 | kN/m | |
| TD : 25.0 µm | 260.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 123 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3956 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RAMLLOY PVB702 | Polyram Ram-On Industries | ABS+Nylon | RAMLLOY |
| SWANCOR Epoxy CP99 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Sylvin 86009-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Petrothene® NA426225 | LyondellBasell Industries | LDPE+EVA | Petrothene® |