Starex TF-0959 T
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dysQBn_Starex-TF-0959-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex TF-0959 T is a Polymethyl Methacrylate Acrylic product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| -- | 0.30 | g/10 min | |
| 220°C/10.0 kg | 15 | g/10 min | |
| Molding Shrinkage - Flow | |||
| -- | 0.30 | % | ASTM D955 |
| 3.20 mm | 0.30 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785, ISO 2039-2 | |
| Pencil Hardness | JIS K5401 | ||
| -- 1 | 3H | ||
| -- 2 | 3H |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2500 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 4 | 55.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 5 | 34.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 6 | 25 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 7 | 2300 | MPa | ASTM D790 |
| -- 8 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 9 | 78.0 | MPa | ASTM D790 |
| -- 10 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 20 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 20 | J/m | ASTM D256 |
| 23°C 12 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 340 | J/m | |
| 23°C, 6.35 mm | 290 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 84.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 77.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 72.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 93.0 | °C | ISO 306/B50 |
| -- | 95.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze (3200 µm) | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90.0 | °C | |
| Desiccant Dryer | 90.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | Condition: 1000g |
| 2 . | Condition: 500g |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 5.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 2.8 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | Thickness: 4 mm |
| 12 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-452HP | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| RAMAPET® P184 | Indorama Ventures PCL | PET | RAMAPET® |
| Europrene® N 3330 GRN | Versalis S.p.A. | NBR | Europrene® |
| HIPTEN® 22003 | HIP-PetroHemija | LDPE | HIPTEN® |
| LNP™ THERMOCOMP™ 2F005 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |