Nylfor® A2 GF/30 H2 W BLACK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nylfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dybgGo_Nylfor-A2-GF-30-H2-W-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced polyamide 66, heat and hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 5.5 | % | ISO 62 |
| Moisture Content | 1.7 | % | ISO 15512 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648 |
| Vicat Softening Temperature | 252 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Impact Copolymer CP420 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| TOTAL Polyethylene LDPE LA 0710 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| EXCELINK 1200B | JSR Corporation | TPV | EXCELINK |
| Hy-Vin® XN78036 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Karina IVORY PVC COMPOUND 70900-35/ 1-F-AC-HSF-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |