Terluran® EHI-7
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dyDHHw_Terluran-EHI-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran® EHI-7 is a medium flow, high impact extrusion grade with super high gloss and superior surface aesthetics. Styrolution' s Terluran® EHI-7 is intended for mono or multilayer sheet making it a perfect fit as a substrate for our weatherable Luran® S ASA. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2170 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 43.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.9 | % | ASTM D638 |
| Fracture, 23°C | 9.2 | % | ASTM D638 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 0.379 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 380 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| Peak Force | 31.0 | J | ASTM D3763 |
| Total Energy | 48.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ISO 306/A50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 92 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 218 - 260 | °C |
| Extrusion instructions |
|---|
| Suggested Max. Regrind: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Battery GPP1001M-P-2986 Grey | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| TECHNO AES 145HA | Techno Polymer America, Inc. | AES | TECHNO AES |
| Nanjing Hongrui PA6 B500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| AFFINITY™ PF 1162G | The Dow Chemical Company | POP | AFFINITY™ |
| Durez® 5019 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |