NOVAPOL® LA-0219-A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dy31GY_NOVAPOL-LA-0219-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL® LA-0219-A is a Low Density Polyethylene material. It is available in North America for foam processing. Important attributes of NOVAPOL® LA-0219-A are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 8.80 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 710 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 296 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | > 0.60 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 150 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 175 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 38 µm, Blown Film | 9.00 | MPa | |
| MD : Break, 38 µm, Blown Film | 18.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 350 | % | |
| TD : Break, 38 µm, Blown Film | 550 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 230 | g | |
| TD : 38 µm, Blown Film | 150 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 40 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Strength | 0.500 | g/3 min | |
| Puncture 1(38.0 µm) | 450 | J/cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGF25/15 42H-BK167A | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Multi-Flex® TPE A7606 UV | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Nanjing Hongrui PC CT1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| BorSafe™ HE3470-LS | Borealis AG | HDPE | BorSafe™ |
| Colorite G Series 9512G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |