LNP™ STAT-KON™ REF42I compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dxYB9s_LNP-STAT-KON-REF42I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-R-86624 Product reorder name: REF42I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.69 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.96 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14700 | MPa | ASTM D638 |
| -- | 13900 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 195 | MPa | ISO 527-2/5 |
| Break 2 | 197 | MPa | ASTM D638 |
| Break | 176 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.6 | % | ISO 527-2/5 |
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 4(50.0 mm Span) | 11500 | MPa | ASTM D790 |
| Flexural Stress | |||
| -- | 264 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 277 | MPa | ASTM D790 |
| Break, 50.0 mm Span 6 | 274 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 7 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 8 | 63 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 22.6 | J | ASTM D3763 |
| -- | 4.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 260 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 247 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 CC TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Qenos PE HD2090 | Qenos Pty Ltd | HDPE | Qenos PE |
| Beamset 770 | Arakawa Chemical Industries, Ltd. | Vinyl Ester | Beamset |
| E-RIALFILL EP 15 S 30 C2 | RIALTI Srl | PP, Unspecified | E-RIALFILL |
| Iupiace® GX1050 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |