WPP PP PPH2UFO-UV DX9 Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dxMd78_WPP-PP-PPH2UFO-UV-DX9-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The properties shown below are typical for a polypropylene homopolymer. This basic product satisfies the needs of many applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 36.0 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1600 | MPa | ASTM D790 |
| -- 3 | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Multi-Axial Instrumented Impact Energy (23°C) | 5.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 13 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Utomer UT380 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Ekalon® 26 E I S | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| ELASTOSIL® AUX PRIMER G 3244 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| Kumho EPS SEPS N16 | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Hifax TYC 1168X E BLACK | LyondellBasell Industries | PP Copolymer | Hifax |