SUPRAN® LFT PA 1350
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® LFT PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dwc1eN_SUPRAN-LFT-PA-1350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% long glass fiber reinforced polyamide 6. High Stiffness & superior mechanical balanced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D648 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 245 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638 |
| Flexural Modulus | 14200 | MPa | ASTM D790 |
| Flexural Strength | 304 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 260 | J/m | |
| 23°C | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 220 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-885ET8 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Bayflex® 110-50 | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| ASTALON™ S3000 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Axiall PVC 19922 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| XENOY™ 6620 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |