RTP 4082 TFE 15
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dwG4ni_RTP-4082-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15200 | MPa | ASTM D638 |
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 259 | MPa | ASTM D790 |
| Coefficient of Friction (With Metal-Dynamic) | 0.18 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 254 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 2mil/in.Wear Factor, K, ASTM D3702: 25E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D3702: 0.18The wear factor and coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 304 - 343 | °C | |
| Middle Temperature | 304 - 343 | °C | |
| Front Temperature | 304 - 343 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGV HZ 15 Black | Radici Plastics | Nylon 6 | Radilon® |
| Andur 9500-AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Hostaform® M15HP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Ducor® 1084K | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| Sylvin 7833-80 Black 294 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |