LNP™ THERMOCOMP™ ZF0049 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dw5XPw_LNP-THERMOCOMP-ZF0049-compound-87849.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZF0049 is a compound based on PPO resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound ZF-1004 FR HP Product reorder name: ZF0049 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.49 | % | ISO 294-4 |
| Flow : 24 hr | 0.28 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 6830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 88.9 | MPa | ASTM D638 |
| Yield | 84.0 | MPa | ISO 527-2 |
| Break | 88.9 | MPa | ASTM D638 |
| Break | 84.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.7 | % | ASTM D638, ISO 527-2 |
| Break | 1.7 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12400 | MPa | ASTM D790 |
| -- | 6600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 241 | MPa | ASTM D790 |
| -- | 118 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 420 | J/m | ASTM D4812 |
| 23°C 3 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.9 | J | ASTM D3763 |
| -- | 3.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 111 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 104 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 5.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® M-1842-GL 31LS | Unipack Plasindo | PVC, Unspecified | polyvic® |
| BITONER® C9 H-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| BMC 350 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Cellophane™ 350P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| PETLIN LD C225Y | PETLIN (MALAYSIA) SDN BHD | LDPE | PETLIN |