LNP™ THERMOCOMP™ AW00A compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dvs8kV_LNP-THERMOCOMP-AW00A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP AW00A is a compound based on Acrylonitrile Butadiene Styrene resin containing Wollastonite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3900 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 49.0 | MPa | |
| -- 4 | 39.0 | MPa | |
| Flexural Strain at Break 5 | 5.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 81.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.9E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P grey homopolymer | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| TAIRIREX GP550N | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| NORYL™ SE100HX resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Polyrocks EP8400S90V-1 | Polyrocks Chemical Co., Ltd | PE, Unspecified | Polyrocks |
| ESTOPLAST XU 430NN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |