LNP™ STAT-KON™ KD000 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dtRepz_LNP-STAT-KON-KD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound K- Product reorder name: KD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 60°C | 1.2 to 1.3 | % | Internal Method |
| Flow : 100°C | 1.5 to 1.6 | % | Internal Method |
| Flow : 24 hr | 1.5 to 3.5 | % | ASTM D955, ISO 294-4 |
| Across Flow : 60°C | 0.90 to 1.0 | % | Internal Method |
| Across Flow : 100°C | 1.1 to 1.2 | % | Internal Method |
| Across Flow : 24 hr | 1.5 to 3.5 | % | ASTM D955, ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.28 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3500 | MPa | ASTM D638 |
| -- | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 58.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Break | 54.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.6 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2 |
| Break | 7.2 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3250 | MPa | ASTM D790 |
| -- | 3200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 95.0 | MPa | ASTM D790 |
| -- | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| 23°C 2 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.00 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 105 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0336G25C002L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Cheng Yu N6G10 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| ENFLEX V1035A | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| Hytrel® HTR4275 BK316 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Sylvin 5210-75 White 1553 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |