Propafilm™ RDP125
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dtQuqi_Propafilm-RDP125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Peelable Seal Differentially Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on one side with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer, the other side coated with an aqueous acrylic dispersion. RDP125 is recommended for use in plain and printed packs. Applications in the cookie, bakery and confectionery industries. Particulaly suitable for V.F.F applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3200 | µm | |
| Seal Strength | Internal Method | ||
| -- 1 | 0.12 | N/mm | |
| -- 2 | 0.14 | N/mm | |
| Seal Initiation Temperature | Internal Method | ||
| -- 3 | 85.0 to 146 | °C | |
| -- 4 | 104 to 146 | °C | |
| Oxygen Permeability (25°C, 0% RH) | 0.74 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 4.0 | g/m²/24 hr | ASTM F1770 |
| Yield | 34.9 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 5 | 3.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Acrylic/Acrylic; 265°F; 2secs; 15psi |
| 2 . | PVdC/PVdC; 265°F; 2secs; 15psi |
| 3 . | Acrylic/Acrylic; 2secs; 15psi |
| 4 . | PVdC/PVdC; 2secs; 15psi |
| 5 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC14-1090 | Spartech Polycom | Nylon 66 | Spartech |
| EnviroTPO 2002 | West Michigan Compounding | TPO | EnviroTPO |
| LNP™ THERMOCOMP™ MB006S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| ALTECH® PC ECO 2020/146 FR GF20 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| SIBUR Synthetic Rubber NBR 3375 | SIBUR | NBR | SIBUR Synthetic Rubber |