Daplen™ EE260AI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dsUwyN_Daplen-EE260AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EE260AI is a 20% mineral-filled compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 14 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 56 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, Injection Molded) | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C, Injection Molded) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C, Injection Molded) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C, Injection Molded) | 1900 | MPa | ISO 178 |
| Flexural Stress (23°C, Injection Molded) | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 70 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 52.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hrs (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 2181 | RTP Company | PEI | RTP |
| ExxonMobil™ PP7011L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| HOPELEX AG-3050 | Lotte Chemical Corporation | PC+ABS | HOPELEX |
| K-vinyl KK-S-FR-A-88 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Karina CLEAR PVC COMPOUND 78/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |