BJB Polyurethane TC-802 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ds8FTU_BJB-Polyurethane-TC-802-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-802 A/B is an easy to use rigid urethane casting material. TC-802 A/B is an extremely low viscosity system with quick demold times. This system also exhibits good physical and heat capabilities. In addition, this system is economically priced. The one-to-one volume ratio makes it perfect for use with dispensing equipment. TC-802 A/B is a great product when ABS-type parts with a quick turnaround are required. Features a non-mercury based catalyst system. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.990 | g/cm³ | |
| -- | 1.06 | g/cm³ | |
| -- 2 | 1.10 | g/cm³ | |
| Specific Volume | 0.957 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time 3(25°C) | 1.7 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.60 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 to 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 910 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 28.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 40 | % | ASTM D638 |
| Flexural Modulus | 1020 | MPa | ASTM D790 |
| Flexural Strength | 41.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 80.6 | °C | |
| 1.8 MPa, Unannealed | 63.9 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 90, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 80.0 | cP | |
| 25°C 5 | 120 | cP | |
| 25°C 6 | 40.0 | cP | |
| Demold Time (25°C) | 10 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Mixed |
| 5 . | Part B |
| 6 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 SI 2 Z | RTP Company | Nylon 66 | RTP |
| Shin-Etsu Elastomer KE-5530U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Adell Polyamide AJ-37 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| LNP™ LUBRICOMP™ DL0039EF compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Sylvin 4200-88 Yellow 433 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |