HiPrene® T150D
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ds4F07_HiPrene-T150D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® T150D is a medium flow olefinic thermoplastic elastomer (TPE-O). This material has excellent impact resistance even at low temperatures. It has been primarily designed for Airbag Cover. This material is available in natural or color-matched, pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Ash Content (600°C) | 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 13.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 420 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 540 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 120 | kJ/m² | ASTM D256 |
| 23°C | No Break | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9740-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TAROBLEND 88 G4 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| VESTAMID® L L1940 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| VECTRA® A515 | Celanese Corporation | LCP | VECTRA® |
| Elastron® G G250.A58.B | Elastron USA, Inc. | SEBS | Elastron® G |