Innova R 970E
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Innova SA |
| Trademark: | Innova |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | drvEFM_Innova-R-970E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Characteristics:
Process:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 4.0 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 3.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | < 0.10 | % | ASTM D570 |
| Saturation, 23°C | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 65 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2050 | MPa | ASTM D638 |
| 23°C | 2000 | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 27.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 70 | % | ASTM D638 |
| Break, 23°C | 75 | % | ISO 527-2 |
| Flexural Strength | |||
| 23°C | 41.0 | MPa | ASTM D790 |
| 23°C | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 160 | J/m | ASTM D256 |
| 23°C | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 86.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525, ISO 306/A50 2 1 |
| -- | 102 | °C | ASTM D1525, ISO 306/B50 3 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 260 | °C | |
| Mold Temperature | 40.0 to 75.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILOY® 210NHBL | Samyang Corporation | PC+ABS | TRILOY® |
| Elvakon® CX15574 | Lucite International Inc. | Acrylic (PMMA) | Elvakon® |
| KetaSpire® KT-850P | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Karina CLEAR PVC COMPOUND -E 78/200-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Starpylen HW 30K ECR | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |