Order Products : sales@su-jiao.com
Generic Biodeg Polymers
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dquaxW_Generic-Biodeg-Polymers.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Biodeg Polymers This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 - 1.45 | g/cm³ | ASTM D792 |
| 23°C | 1.23 - 1.30 | g/cm³ | ISO 1183 |
| -- | 0.990 - 1.42 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.43 - 25 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 2.4 - 15 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.024 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 40 - 89 | ASTM D2240 | |
| 23°C | 78 - 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 712 - 1300 | MPa | ASTM D638 |
| 23°C | 122 - 3460 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 9.68 - 39.1 | MPa | ASTM D638 |
| Yield, 23°C | 9.00 - 50.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 7.28 - 35.3 | MPa | ASTM D638 |
| Fracture, 23°C | 4.00 - 29.9 | MPa | ISO 527-2 |
| 23°C | 10.7 - 32.8 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 0.70 - 8.2 | % | ISO 527-2 |
| Fracture, 23°C | 1.2 - 110 | % | ASTM D638 |
| Fracture, 23°C | 0.67 - 21 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 212 - 2480 | MPa | ASTM D790 |
| 23°C | 215 - 3560 | MPa | ISO 178 |
| Flexural Stress (23°C) | 6.00 - 70.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 56.5 - 131 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 8.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 4.8 - 36 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 21 - 78 | J/m | ASTM D256 |
| 23°C | 9.5 - 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 42.6 - 118 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 55.0 - 56.7 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 39.0 - 66.6 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 45.0 - 137 | °C | ASTM D1525 |
| -- | 98.2 - 135 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 86.0 - 153 | °C | |
| -- | 89.0 - 215 | °C | ASTM D3418 |
| -- | 141 - 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Drying Time | 2.0 - 7.2 | hr | |
| Suggested Max Moisture | 0.20 - 2.5 | % | |
| Rear Temperature | 45.0 - 185 | °C | |
| Middle Temperature | 70.0 - 175 | °C | |
| Front Temperature | 115 - 190 | °C | |
| Nozzle Temperature | 130 - 203 | °C | |
| Processing (Melt) Temp | 162 - 195 | °C | |
| Mold Temperature | 12.5 - 45.8 | °C | |
| Screw Speed | 80 - 138 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Biodeg PolymersThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 119 - 185 | °C | |
| Cylinder Zone 2 Temp. | 144 - 180 | °C | |
| Cylinder Zone 3 Temp. | 154 - 185 | °C | |
| Cylinder Zone 4 Temp. | 145 - 195 | °C | |
| Melt Temperature | 162 - 195 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Biodeg PolymersThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2407 | Covestro - Polycarbonates | PC | Makrolon® |
| Rhelon G2533-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| StarTUFF TF 65-HR-1 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| Sylvin 8336-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Geon™ Vinyl Flexible B6000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |