KPOL-NYLON K-NY6/40CF

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-NYLON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dqlBfh_KPOL-NYLON-K-NY6-40CF.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Standard Polyamide 6 / 6.6 Copolymer

Characteristics

KPOL® NY6/40CF is a copolymer of Nylon 6 high viscosity, which has excellent characteristics for extruded films, co-extruded multilayer packaging. The chemical combination of monomers, confers a greater ability to orient the film, with optimization and high degree of luster, transparency, gas barrier and high tear resistance.

Applications

The grade is suitable for a wide field of film and extrusion applications. This material has following features: Outstanding processability, Good mechanical properties, Good transparency and Good puncture resistance.

General Information
Features	Copolymer Gas Barrier Good Processability Good Tear Strength High Viscosity Puncture Resistant
Uses	Film Packaging
Appearance	Clear/Transparent
Processing Method	Extrusion Film Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.12	g/cm³	ASTM D792
Relative Viscosity - SAV @ 96% Sulfuric Acid
--	4.00		ISO 307
--	4.00		ASTM D789

Films	Nominal Value	Unit	Test Method
Oxygen Transmission Rate (23°C, 0% RH)	25	cm³/m²/24 hr	ASTM D3985
Water Vapor Transmission Rate (40°C, 90% RH)	140	g/m²/24 hr	ISO 15106-3

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	202	°C	ASTM D2117

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	70		ASTM D523
Haze	24	%	ASTM D1003

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC P8170	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RTP 1481 N TFE 15	RTP Company	PESU	RTP
RTP 107 HI UV	RTP Company	PP Copolymer	RTP
Jiangsu Sinarise JM8211	Jiangsu Sinarise New Material Technology Co., Ltd	TPE	Jiangsu Sinarise
MAJORIS DM400 - 8229	AD majoris	PP, Unspecified	MAJORIS