XAREC™ S105
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dqfoEb_XAREC-S105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XAREC™ S105 is a Syndiotactic Polystyrene (SPS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C | 1.0 to 1.2 | % | |
| Across Flow : 150°C | 1.7 to 1.9 | % | |
| Flow : 80°C | 0.70 to 0.90 | % | |
| Flow : 150°C | 1.7 to 1.9 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | > 100 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | > 100 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| CLTE | TMA | ||
| Flow : -30 to 30°C | 8.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | < 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) 3 | PLC 0 | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | Mold temperature: 80°C |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starglas FF004 | Eurostar Engineering Plastics | HDPE | Starglas |
| Styrolution PS 158K | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Adsyl 3 C 30 F HP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| LUVOCOM® 2205-7123 VP | Lehmann & Voss & Co. | PAEK | LUVOCOM® |
| TABOREN® PH 42 T 20-990 | SILON s.r.o. | PP Homopolymer | TABOREN® |