DOWLEX™ 2042EC
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dq7plo_DOWLEX-2042EC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2042EC Polyethylene Resin is an ethylene/octene-1 copolymer suitable for the production of blown film requiring good tear strength and outstanding toughness with good stiffness and temperature resistance. Note: DOWLEX 2042EC Polyethylene Resin should comply with FDA regulation 177.1520, Canadian HPFB No Objection (With Limitations) and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Please, contact your nearest Dow office for food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant (Compression Molded) | 340 | MPa | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy (25 µm) | 1.00 | J | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 14.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 17.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 42.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 830 | % | ASTM D882 |
| TD : Break, 25 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25 µm | 100 | g | ASTM D1922 |
| TD : 25 µm | 620 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 24.9 µm) | 30 | ASTM D2457 | |
| Haze (24.9 µm) | 12 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Tubular Film Extrusion: Melt Temperature: 190 to 240°C Blow-Up Ratio Range: 1.5 to 3:1 Recommended Gauge Range: 10 to 150 µm |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ741 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Resan SAN | Polimarky Spolka Jawna | PS (GPPS) | Resan |
| Yuyao PPO GFN2-701 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Andur 6 APLM/Curene® 442 | Anderson Development Company | PCL | Andur |
| Kumho ABS HU621 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |