Tecomid® NB40 NL FN70
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecomid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dq2yMu_Tecomid-NB40-NL-FN70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6, unfilled, flame retardant - halogen (RoHS compliant), natural, suitable for IEC 60335-1 (E/E devices used for home appliances) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.90 | % | Internal method |
| Flow direction | 0.90 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % | ISO 62 |
| Moisture Content | % | ISO 960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3750 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B |
| Melting Temperature 1 | 223 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evolue™-H SP50800P | Prime Polymer Co., Ltd. | HDPE | Evolue™-H |
| FLEXAREN® 18020 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Hostalen ACP 5231 D | LyondellBasell Industries | HDPE | Hostalen |
| 3M™ Dyneon™ Fluoroelastomer FE 5624Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 9067-85LMW GREY 9269 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |